China Supplier ASTM A213 304 316L 321 310S Bright Mirror Polished Stainless Steel Round Square Rod

304 stainless steel rod is an alloy steel material with pitting corrosion resistance, high temperature resistance, creep resistance and high strength

-Implementation standards
Chinese standard:
Hot rolled and forged stainless steel rods: GB/T1220-2007
Cold processed stainless steel rod: GB4226-2009
American standard:
Stainless Steel Rods and Shapes Standard: ASTM A276-2011
General standard for stainless steel bars, billets and forgings ASTM A484-2011
Standard for easily machined stainless steel rods ASTM A582-2011
ASME SA276-2010, ASME SA484-2010

ASTM A484/A484M, ASTM A213/213A, ASTM A269/269M

Excellent pitting corrosion resistance and excellent high temperature creep strength.

2. Features 1) The cold-rolled product has good gloss and beautiful appearance; 2) Added Mo, excellent corrosion resistance, especially pitting corrosion resistance; 3) Excellent high temperature strength; 4) Excellent work hardening (weak magnetism after processing ) 5) Non-magnetic in solid solution state; 6) Compared with 304 stainless steel, the price is higher.
3. Scope of application: pipes, heat exchangers, food industry, chemical industry, etc.

304 stainless steel round rod, 304 stainless steel capillary rod
Brand: 0Cr18Ni9 (0Cr19Ni9)
Element
C: ≤0.07, Si: ≤1.0,
Mn: ≤2.0,
Cr: 17.0～19.0,
Ni: 8.0~11.0,
S: ≤0.03,
P: ≤0.035.
Tensile strength (Mpa) 620 MIN
Yield strength (Mpa) 310 MIN
Elongation (%) 30 MIN
Area reduction (%) 40 MIN
The density of 304 stainless steel is 7.93 g/cm3. Austenitic stainless steel generally uses this value. 304 chromium content (%) 18–20. 304 is equivalent to my country’s 0Cr19Ni9 (0Cr18Ni9) stainless steel. 304 stainless steel is a universal stainless steel material. The anti-rust performance is stronger than that of 200 series stainless steel materials. It is also relatively good in terms of high temperature resistance and can reach temperatures as high as 1000-1200 degrees. 304 stainless steel has excellent stainless corrosion resistance and good intergranular corrosion resistance. For oxidizing acids, it was found in experiments that 304 stainless steel has strong corrosion resistance in nitric acid below the boiling temperature with a concentration of ≤65%. It also has good corrosion resistance to alkaline solutions and most organic and inorganic acids.

-Weight calculation formula

Weight (kg)=Diameter (mm)*Diameter (mm)*Length (m)*0.00623
Specific gravity of stainless steel:
●Chromium stainless steel takes 7.75 tons/M3
●Chromium-nickel stainless steel is 7.93 tons/M3
●Iron extraction 7.87 tons/M3
Stainless steel plate theoretical weight calculation formula
Theoretical weight of steel products Weight (kg) = Thickness (mm) × Width (mm) × Length (mm) × Density value

-American and national standard thickness:
28GA=0.015inches=0.38mm
26GA=0.018inches=0.46mm
24GA=0.024inches=0.61mm
22GA=0.030inches=0.76mm
20GA=0.036inches=1.00mm
18GA=0.048inches=1.25mm
16GA=0.060inches=1.60mm
14GA=0.075inches=2.00mm
12GA=0.105inches=2.70mm

Materials: 304, 304L, 321, 316, 316L, 310S, 630, 1Cr13, 2Cr13, 3Cr13, 1Cr17Ni2, duplex steel, antibacterial steel and other materials!

304 (18Cr-8Ni) material:

As a widely used steel, it has good corrosion resistance, heat resistance, low strength and mechanical properties; good hot workability such as stamping and bending, and no heat treatment phenomenon (no heat treatment phenomenon) Gloss, uses: Household products (Class 1 and 2 sanitary ware, wardrobes, indoor wiring, water heaters, boilers, bathtubs), auto parts (windshield wipers, mufflers, molded products), medical equipment, building materials, chemistry, food industry, agriculture, ships part.

-Stainless Steel Rod Grade:

200 stainless steel series: 201, 202 (chromium, nickel, manganese-austenitic stainless steel)
300 stainless steel series: 301, 302, 302HQ, 303, 304, 304L, 304F, 304HC, 316, 316L, 316F, 316S, 316Ti, 310, 310S, 314, 314L, 317, 317L, 321 (chromium, nickel-austenitic body stainless steel)
400 stainless steel series: 410, 420, 420J2, 430, 430F, 431 (ferritic and martensitic stainless steel)

Note: L stands for low carbon. For example, 304L has lower carbon content than 304. H and S represent high temperature resistance. For example, 310S is more heat resistant than 310, and 304H is more heat resistant than 304.
Stainless steel rods are divided into round rods, hexagonal rods, square rods, flat rods, round rods and solid rods. The ones with glossy surfaces are more expensive than those with black leather surfaces. 303 is a unique material in rods. It is an easy-to-turn (cut) type material and is mainly used for automatic lathe cutting. In addition: 304F, 303CU, and 316F are also easy-to-cut materials. Specifications: Ф1mm～Ф280mm.